Due to its non-destructive characteristic, nuclear magnetic resonance (NMR) spectroscopy was used to study the fiber saturation point (FSP) of Pseudotsuga menziesii before and after heat treatment. The bound water amount in saturated wood cell wall was determined by analysis of T2 relaxation time distributions measured using GPMG (Carr-Purcell-Meiboom-Gill) sequence at -3℃ and 25℃. Results showed that the FSP of Pseudotsuga menziesii treated with various temperatures are 32.82% (180℃), 29.40% (200℃), 24.90% (220℃) and 38.76% (untreated), which indicate that FSP of Pseudotsuga menziesii decreases with increased heat treatment temperature. This study reflects that NMR could provide detailed information about wood water distribution rapidly and efficiently.
ZHOU Fan-ding
,
GAO Xin
,
CAI Jia-bin
,
ZHUANG Shou-zeng
,
ZHOU Hong-jie
. Determination of Treated and Control Wood on Fiber Saturation Point by Low-Field NMR Technology[J]. Chinese Journal of Magnetic Resonance, 2017
, 34(1)
: 108
-114
.
DOI: 10.11938/cjmr20170113
[1] HILL C A S. Wood modification:Chemical, thermal and other processes[M]. Chichester:Wiley, 2006
[2] XIE Y, QILIANG F, QINGWEN W, et al. Effects of chemical modification on the mechanical properties of wood[M]. Eur J Wood Prod, 2003, 71(4):401-416
[3] LIAO G Z, XIAO L Z. Research on porous of exponential inversion Factors Influencing by NMR relaxation measurements[J]. Geophysics, 2007, 50(3):932-983. 廖广志, 肖立志. 孔隙介质核磁共振弛豫测量多指数反演影响因素研究[J]. 地球物理学报, 2007, 50(3):932-983
[4] GAO X, ZHUANG S Z. Bound water content in saturated wood cell wall determined by nuclear magnetic resonance spectroscopy[J]. Chinese J Magn Reson, 2015, 32(4):671-676. 高鑫, 庄寿增. 利用核磁共振测木材吸着水饱和含量[J]. 波谱学杂志, 2015, 32(4):671-676.
[5] BABIAK M, KUDELA. A contribution to the definition of the fiber saturation point[J]. Wood Sci, Technol, 29(3):217-226.
[6] TELKKI V V, YLINIEMI M, JOKISAARI J. Moisture in softwoods:Fiber saturation point,hydroxyl site contentand the amount ofmicropores as determined from NMR relaxation time distributions[J]. Holzforschung, 2013, 67(3):291-300.
[7] MA D Y, WANG X M, ZHANG M H. Mechanism of water sorption during adsorptionprocess of wood studied by NMR[J]. Chinese J of Magn Reson, 2011, 28(1):135-141. 马大燕, 王喜明, 张明辉. 核磁共振研究木材吸着过程水分吸附机理[J]. 波谱学杂志, 2011, 28(1):135-141.
[8] AKSNES D W, KIMTYS L. 1H and 2H NMR studies of benzene confined in porous solids:Melting point depression and poresizedistribution[J]. Solid State Nucl Mag, 2004, 25(1-3):146-152.
[9] LI C, ZHANG M H, YU J F. Determining wood moisture content by free inductiondecay of nuclear magnetic resonance[J]. Journal of Beijing Forestry University, 2012, 34(4):142-145. 李超, 张明辉, 于建芳. 利用核磁共振自由感应衰减曲线测定木材含水率[J]. 北京林业大学学报, 2012, 34(4):142-145.
[10] 肖立志. 核磁共振成像测井与岩石核磁共振及其应用[M]. 北京:科学出版社, 1998.
[11] KEKKONEN P M, YLISASSI A, TELKKI V V. Absorption of water in thermally modified pine wood as studied by nuclear magnetic resonance[J]. J Phys Chem C, 2004, 118(4):2146-2153.
[12] SIMPSON L A, BARTON A F M. Determination of the fiber saturation point in whole wood using differential scanning calorimetry[J]. Wood Sci, Technol, 1991, 25:301-308.
[13] ZAUER M, KRETZSCHMAR J, GROBMANN L, et al. Analysis of the pore-size distribution and fiber saturationpoint of native and thermally modified wood using differential scanning calorimetry[J]. Wood Sci Technol, 2014, 48(1):177-193.
[14] 赵喜平. 磁共振成像系统的原理及其应用[M]. 北京:科学出版社, 2000.
[15] DING T, GU L B, LIU X. Influence of steam pressure on chemical changes of heat-treated Mongolian pine wood[J]. Bio Resources, 2011, 6(2):1880-1889.
[16] Rowell R M. Handbook of wood chemistry and wood composites[M]. Boca Raton:CRC Press, 2005.
[17] GINDL W, ZARGAR-YAGHUBI F, WIMMER R. Impregnation of softwood cell walls with melamine-formaldehyde resin[J]. Bioresour Technol, 2003, 87(3):325-330.
[18] ZHANG S C, QI H C. Effect of high temperature steam treatment on the crystalline properties of wood[J]. Journal of Nanjing Forestry University, 2010, 34(5):164-166. 张士成, 齐华春. 高温过热蒸汽处理对木材结晶性能的影响[J]. 南京林业大学学报:自然科学版, 2010, 34(5):164-166.
[19] BHUIYAN M T R, HIRAI N, SOBUE N. Changes of crystallinity in wood cellulose by heat treatment under driedandmoist conditions[J]. J Wood Sci, 2000, 46(6):431-436.
[20] AKGÜL M, GÜMÜSKAYA E, KORKUT S. Crystalline structure of heattreated Scots pine (Pinus sylvestrisL) a-nd Uluda ? fir[Abies nordmanniana (Stev.)subsp.bornmuelleriana(Mattf.)] wood[J]. Wood Sci Technol, 2007, 41(3):281-289.
[21] TJEERDSMA B F, BOONSTRA M, PIZZI A, et al. Characterisation of thermally modified wood:Molecular reasons for wood performance improvement[J]. Holz als Roh-und Werkstoff, 1998, 56(3):149-153.
[22] WEILAND J J, GUYONNET R. Study of chemical modifications and fungi degradation of thermally modified wood using DRIFT spectroscopy[J]. Holz als Roh-und Werkstoff, 2003, 61(3):216-220.
[23] WIKBERG H, MAUNU S L. Characterisation of thermally modied hard-and softwoods by 13C CPMAS NMR[J]. Carbohydrate Polymers, 2004, 58(4):461-466.
[24] BORREGA M K, RENLAMPI P P. Hygroscopicity of heat-treated Norway spruce (Picea abies) wood[J]. Holz als Roh-und Werkstoff, 2010, 68(2):233-235.
[25] JACKSON C L, MCKENNA G B. The melting behavior of organic materials confined in porous solid[J]. Chem Phys, 93:9002-9011.
[26] WANG Z P, WANG T. The principle and application of NMR freezing hole method[J]. Journal of material, 2013, 27(1):129-133. 王中平, 王弢. 简述核磁共振冷冻测孔法的原理及应用[J]. 材料导报, 2013, 27(1):129-133.
[27] OSTLUND A, KOHNKE T, NORDSTIERNA L, et al. NMR cryopormetry to study the fiber wall structure and the effect of drying[J]. Cellulose, 2010, 17:321-328.
[28] KEKKONEN P M, YLISASSI A, TELKKI V V. Absorption of water in thermally modified pine wood as studied by NMR[J]. J Phys Chem C, 2013, 118:2146-2153.